多弧离子镀沉积TiN-Cu复合膜
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

TG 174.44

基金项目:

四川省科技厅科技支撑计划(2014GZ0004)


TiN-Cu composite films deposited by multi-arc ion plating
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    摘要:利用多弧离子镀的方法,分别在不同弧电流和沉积时间下,在不锈钢基体上沉积TiN-Cu复合膜;对薄膜表面形貌、截面形貌、相组成和硬度进行表征。结果表明,复合膜中的Cu含量、沉积条件对薄膜微观结构和硬度有重要的影响。金属Cu的加入,阻止了TiN柱状晶的生长,改变了纯TiN薄膜的择优取向;当沉积时间为2h,脉冲负偏压为200V时,Cu含量为12.96at%,复合膜硬度达到最大值为2976HV。

    Abstract:

    Abstract:TiN-Cu composite films were deposited on stainless substrates at different arc current and deposited time, using a type of multi-arc ion plating system. The surface morphology, cross-sectional morphology, phase structure and hardness of composite films were characterized. The results show that, with increasing in the Cu content, metallic Cu can inhibit the columnar growth and change the preferred orientation of pure TiN films. The highest value of composite film hardness is obtained with 12.96at% Cu, when deposited time is 2h and negative pulse bias is 200V. Cu content and deposition condition have a great impact on the hardness of composite films.

    参考文献
    相似文献
    引证文献
引用本文

引用本文格式: 杨红,刘进,石云龙. 多弧离子镀沉积TiN-Cu复合膜[J]. 四川大学学报: 自然科学版, 2017, 54: 376.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-01-19
  • 最后修改日期:2016-02-18
  • 录用日期:2016-03-07
  • 在线发布日期: 2017-03-09
  • 出版日期:
通知
自2024年3月6日起,《四川大学学报(自然科学版)》官网已迁移至新网站:https://science.scu.edu.cn/,此网站数据不再更新。
关闭