CaGd3F11:Eu3+超小纳米晶的制备及其发光性质研究
DOI:
作者:
作者单位:

作者简介:

通讯作者:

中图分类号:

0626

基金项目:

市自然科学基金


Synthesis and luminescence of Ultrasmall CaGd3F11:Eu3+ nanocrystals
Author:
Affiliation:

Fund Project:

  • 摘要
  • |
  • 图/表
  • |
  • 访问统计
  • |
  • 参考文献
  • |
  • 相似文献
  • |
  • 引证文献
  • |
  • 资源附件
  • |
  • 文章评论
    摘要:

    以无水氯化钙、稀土硝酸盐、正辛醇为原料,以正辛胺和油酸为表面活性剂,通过控制不同的反应条件,采用溶剂热法制备出形貌均匀的CaGd3F11:Eu3+纳米发光材料。用X射线衍射(XRD)、透射电子显微镜(TEM)和荧光分光光度计对合成的纳米晶的粒径、形貌和光学性质进行了表征。结果表明CaGd3F11纳米晶的结晶度良好且尺寸均匀(约5 nm),其作为基质材料,掺杂Eu3+表现出很强的荧光发射。

    Abstract:

    CaGd3F11:Eu3+ nanocrystals with the morphologies of nanoparticles were prepared by octylamine and oleic acid as capping ligands, and anhydrous calcium chloride, rare earth nitrate, n-octanol as the raw materials with solvothermal method. The products were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM) and fluorescence spectrophotometer. The results indicate that CaGd3F11 nanocrystals are well-crystallized and their sizes are uniform (about 5 nm). As a luminescence host, it shows higher emitting intensity with Eu3+ doping.

    参考文献
    相似文献
    引证文献
引用本文

引用本文格式: 田婧,罗华锋,王强. CaGd3F11:Eu3+超小纳米晶的制备及其发光性质研究[J]. 四川大学学报: 自然科学版, 2018, 55: 367.

复制
分享
文章指标
  • 点击次数:
  • 下载次数:
  • HTML阅读次数:
  • 引用次数:
历史
  • 收稿日期:2016-07-17
  • 最后修改日期:2016-09-02
  • 录用日期:2016-09-03
  • 在线发布日期: 2018-03-12
  • 出版日期:
通知
自2024年3月6日起,《四川大学学报(自然科学版)》官网已迁移至新网站:https://science.scu.edu.cn/,此网站数据不再更新。
关闭